Chemical Composition | |||||||
Gulu | Ndi% | Ku% | Fe% | Mn% | C% | Si% | S% |
mphindi 63 | 28-34 | Max 2.5 | Kuchuluka kwa 2.0 | Kuchuluka kwa 0.30 | Kuchuluka kwa 0.50 | Mtengo wapatali wa magawo 0.024 |
Monel 400 International Brand | ||||
USA | GE | UK | FR | |
UNS | SEW VDIUV | BS | AFNOR | |
Mtengo wa 400 | N04400 | W.Nr.2.4360 NiCu30Fe | ndi 12 | Nd 30 |
Zakuthupi | ||
Gulu | Kuchulukana | Melting Point |
Mtengo wa 400 | 8.83g/cm3 | 1300ºC-1390ºC |
Mechanical Properties | ||||
Aloyi | Kulimba kwamakokedwe (Rm N/mm2) | Zokolola mphamvu (RP0.2N/mm2) | Kutalikira (A5%) | HB |
Mtengo wa 400 | 480 | 170 | 35 | ≥331 |
Production Standard | |||||
Malo | Kupanga | Chitoliro | Mapepala/ Mzere | Waya Wowotcherera | |
Standard | Chithunzi cha ASTM B164 | Chithunzi cha ASTM B564 | Chithunzi cha ASTM B165 | Chithunzi cha ASTM B127 | ERNiCu-7 |
Waya Wina Wothira Mafuta Otentha
Kanthu | Zomwe zili ndi mankhwala | Zn | Cd | Pb | Fe | Cu | Ndalama Zonse |
zinc woyera | Mtengo mwadzina | ≥99.995 | ≤0.002 | ≤0.003 | ≤0.002 | ≤0.001 | 0.005 |
Kanthu | Mtengo wa 625 | N95Al5 | Mtengo wa 45CT | Mtengo wa 400 | Mtengo wa 500 | Mtengo wa HC-276 | Mtengo wa Cr20Ni80 |
C | ≤0.05 | ≤0.02 | 0.01-0.1 | ≤0.04 | ≤0.25 | ≤0.02 | ≤0.08 |
Mn | ≤0.4 | ≤0.2 | ≤0.2 | 2.5-3.5 | ≤1.5 | ≤1.0 | ≤0.06 |
Fe | ≤1.0 | N / A | ≤0.5 | ≤1.0 | ≤1.0 | 4.0-7.0 | N / A |
P | ≤0.01 | ≤0.01 | ≤0.01 | ≤0.01 | ≤0.01 | ≤0.01 | ≤0.02 |
S | ≤0.01 | ≤0.01 | ≤0.01 | ≤0.01 | ≤0.01 | ≤0.01 | ≤0.01 |
Si | ≤0.15 | ≤0.2 | ≤0.2 | ≤0.15 | ≤0.5 | ≤0.08 | 0.75-1.6 |
Cu | N / A | N / A | N / A | kupuma | 27-33 | N / A | N / A |
Ni | kupuma | kupuma | kupuma | 65-67 | kupuma | kupuma | kupuma |
Co | N / A | N / A | N / A | N / A | N / A | N / A | N / A |
Al | ≤0.4 | 4-5 | N / A | ≤0.5 | 2.3-3.15 | N / A | N / A |
Ti | ≤0.4 | 0.4-1 | 0.3-1 | 2.0-3 | 0.35-0.85 | N / A | N / A |
Cr | 21.5-23 | ≤0.2 | 42-46 | N / A | N / A | 14.5-16 | 20-23 |
Nb | 3.5-4.15 | N / A | N / A | N / A | N / A | N / A | ≤1.0 |
Mo | 8.5-10 | N / A | N / A | N / A | N / A | 15-17 | N / A |
V | N / A | N / A | N / A | N / A | N / A | ≤0.35 | N / A |
W | N / A | N / A | N / A | N / A | N / A | 3.0-4.5 | N / A |
Zonyansa | ≤0.5 | ≤0.5 | ≤0.5 | ≤0.5 | ≤0.5 | ≤0.5 | ≤0.5 |
3 C276matenthedwe kupopera waya
Mayina Odziwika: Oxford Alloy® C-276 FM C-276 Techalloy 276
Muyezo: AWS A5.14, ERNiCrMo-4/ ASME II, SFA-5.14, UNS N10276 Werkstoff Nr. 2.4886 ISO SNi6276 Europe NiCrMo16Fe6W4
KUPANGA KWA CHEMICAL(%)
C | Si | Mn | S | P | Ni | Co |
≤0.02 | ≤0.08 | ≤1.0 | ≤0.03 | ≤0.04 | Mpumulo | ≤2.5 |
W | V | Fe | Cu | Cr | Mo | ena |
3.0-4.5 | ≤0.35 | 4.0-7.0 | ≤0.5 | 14.5-16.5 | 15-17 | <0.5 |