China Constantan Flat Wire Copper Nickel Alloy 6j40 Riboni 0.4*2mm Kupanga ndi Fakitale

Constantan Flat Waya Copper Nickel Alloy 6j40 Riboni 0.4*2mm

Kufotokozera Kwachidule:

Constantan Flat Waya Copper Nickel Alloy 6j11 Riboni 0.4*2mm

Kukaniza (200C μ Ω. m): 0.1
Kutentha Kwambiri Kogwira Ntchito (0C): 200
Mphamvu Yokoka (Mpa): ≥ 250
Malo osungunuka (0C): 1095
Kuchulukana (g/cm3):8.9
TCR x10-6/ 0C (20~600 0C): < 100

Satifiketi:ISO 9001

Kukula:Zosinthidwa

dzina la malonda:Aloyi wa Nikeli wa Mkuwa 6j11

ntchito:makampani

zinthu:aloyi

mbali:kukana kwakukulu

ntchito:kukhazikika bwino kwa mawonekedwe

kulemera:zochokera

kukula:monga momwe kasitomala amafunira

mtundu:bulauni

mawonekedwe:waya

MOQ:20kg

Tumizani imelo kwa ife

Tsatanetsatane wa Zamalonda

FAQ

Ma tag a Zamalonda

Constantan Flat Wire Copper Nickel Alloy Yatsopano 6j11 Riboni 0.4*2mm

Khalidwe	Kukana (200C μΩ .m)	Kutentha Kwambiri Kogwira Ntchito (0C)	Mphamvu Yokoka (Mpa)	Malo osungunuka (0C)	Kuchulukana (g/cm3)	TCR x10-6/ 0C (20~600 0C)	EMF vs Cu (μ V/ 0C) (0~100 0C)
Dzina la Aloyi
NC003 (CuNi1)	0.1	200	≥ 250	1095	8.9	< 100	-12

Katundu Wathupi	Chiyerekezo	Ndemanga
Kuchulukana	8.94 g/cc
Katundu wa Makina	Chiyerekezo	Ndemanga
Mphamvu Yolimba, Yopambana	262 – 531 MPa
Mphamvu Yokoka, Kupereka	276 – 524 MPa	Kutengera ndi mkwiyo
Kutalika pa nthawi yopuma	46.0%	mu 50.8 mm.
Modulus ya Elasticity	115 GPa
Chiŵerengero cha Poissons	0.310	Kuwerengera
Kutha kugwira ntchito	20%	UNS C36000 (mkuwa wodula momasuka) = 100%
Shear Modulus	44.0 GPa
Katundu Wamagetsi	Chiyerekezo	Ndemanga
Kukana kwa Magetsi	0.0000120 ohm-cm @Kutentha 20.0 ° C
Katundu wa Kutentha	Chiyerekezo	Ndemanga
CTE, yolunjika	17.5 µ m/m-° C @Temperature 20.0 – 300 ° C
Mphamvu Yotentha Yapadera	0.380 J/g-° C
Kutentha kwa Matenthedwe	64.0 W/mK @Kutentha 20.0 ° C
Malo Osungunuka	< = 1125 ° C	Liquidus
Liquidus	1125 ° C
Katundu Wokonza	Chiyerekezo	Ndemanga
Kutentha kwa Annealing	565 – 815 ° C
Kutentha Kogwira Ntchito Kotentha	815 – 950 ° C
Katundu wa Zinthu Zopangira	Chiyerekezo	Ndemanga
Mkuwa, Cu	> = 91.2%
Chitsulo, Fe	1.30 – 1.70%
Mtsogoleri, Pb	< = 0.050 %
Manganese, Mn	0.30 – 0.80%
Nickel, Ni	4.80 – 6.20%
Zinki, Zn	< = 1.0 %

Kuchuluka kwa Mankhwala a CuNi44, %

Ni	Mn	Fe	Si	Cu	Zina	Malangizo a ROHS
						Cd	Pb	Hg	Cr
44	1%	0.5	-	Mbala	-	ND	ND	ND	ND

Katundu wa Makina

Kutentha Kwambiri kwa Utumiki Wosalekeza	400ºC
Kukhazikika kwa kutentha pa 20ºC	0.49±5%ohm mm2/m
Kuchulukana	8.9 g/cm3
Kutentha kwa Matenthedwe	-6 (Zambiri)
Malo Osungunuka	1280ºC
Mphamvu Yokoka, N/mm2 Yophatikizidwa, Yofewa	340~535 Mpa
Mphamvu Yolimba, N/mm3 Yozungulira Yozizira	680~1070 Mpa
Kutalika (kupindika)	25% (Mphindi)
Kutalika (kozizira kozungulira)	≥Mphindi)2% (Mphindi)
EMF vs Cu, μV/ºC (0~100ºC)	-43
Kapangidwe ka Micrographic	austenite
Katundu wa Maginito	Ayi