China 1.2mm 1.6mm 2.4mm 3.17mm Aluminiyamu MIG TIG Welding Waya Ndodo Er4043 Er4047 Er5356 Er5183 Kupanga ndi Fakitale

1.2mm 1.6mm 2.4mm 3.17mm Aluminium MIG TIG Welding Waya Ndodo Er4043 Er4047 Er5356 Er5183 Chithunzi Chowonetsedwa

1.2mm 1.6mm 2.4mm 3.17mm Aluminiyamu MIG TIG Welding Waya Ndodo Er4043 Er4047 Er5356 Er5183

Kufotokozera Kwachidule:

1.2mm 1.6mm 2.4mm 3.17mm Aluminiyamu MIG TIG Welding Waya Ndodo Er4043 Er4047 Er5356 Er5183

ER4043 5% zili mu Si, zotayidwa pakachitsulo aloyi kuwotcherera waya, ali fluidity wabwino.
Amagwiritsidwa ntchito powotcherera popangira ndi kuponyera zida chifukwa chopanda kumva kung'ung'udza kotentha.
Ndizosavuta kupanga brittle Mg2Si mumsoko wowotcherera panthawi yowotcherera, zomwe zimachepetsa kulimba kwa pulasitiki ndi dzimbiri la olowa.
Kuwotcherera ndi kokongola komanso kowala, arc ndi yokhazikika, spatter ndi yaying'ono, koma pambuyo pa anodizing, mtunduwo ndi wosiyana ndi zitsulo zoyambira.

Utali Wautali:10-20 mm

Phukusi:0.5kg/1kg/5kg/7kg

Kufotokozera:0.8-3.2 mm

HS kodi:8311300000

Mphamvu Zopanga:150ton / Mwezi

Mphamvu Zomaliza:462MPa

Titumizireni imelo

Tsatanetsatane wa Zamalonda

FAQ

Zolemba Zamalonda

Zokhazikika: AWS A5.10 Mtengo wa ER4043	Chemical Composition%
	Si	Fe	Cu		Mn	Zn	Zina				AL
Gulu Mtengo wa ER4043	4.5 - 6.0	≤ 0.80	≤ 0.30		≤ 0.05	≤ 0.10	-				Mpumulo
Mtundu	Spool (MIG)					Tube (TIG)
Kufotokozera (MM)	0.8,0.9,1.0,1.2,1.6,2.0					1.6,2.0,2.4,3.2,4.0,5.0
Phukusi	S100/0.5kg S200/2kg S270,S300/6kg-7kg S360/20kg					5kg / bokosi 10kg / bokosi kutalika: 1000MM
Mechanical Properties	Kutentha kwa Fusion ºC		Zamagetsi Mtengo wa IACS	Kuchulukana g/mm3		Tensile Mpa		Zotuluka Mpa		Elongation %
	575-630		42%	2.68		130-160		70-120		10-18
	Diameter(MM)		1.2			1.6			2.0
MIG Kuwotcherera	Welding Panopa - A		180-300			200-400			240-450
	Kuwotcherera Voltage - V		18-26			20-28			22-32
TIG Kuwotcherera	Diameter (MM)		1.6 - 2.4			2.4 - 4.0			4.0 - 5.0
	Welding Panopa - A		150-250			200-320			220-400
Kugwiritsa ntchito	Yalimbikitsa kuwotcherera 6061 ,6XXX mndandanda;3XXXndi2XXX mndandanda wa aluminiyamu aloyi.
Zindikirani	1, mankhwala akhoza kusungidwa kwa zaka ziwiri pansi pa chikhalidwe fakitale kulongedza ndi kusindikizidwa, ndi kulongedza katundu kumatha kuchotsedwa kwa miyezi itatu pansi pa malo omwe ali mumlengalenga. 2,Zogulitsa ziyenera kusungidwa mu mpweya wabwino, wowuma komanso malo. 3, waya atachotsedwa phukusi, tikulimbikitsidwa kuti chivundikiro choyenera cha fumbi kuikidwa pamwamba pa waya.

Mndandanda wa kuwotcherera kwa almunium alloy:

Kanthu	AWS		Aluminium Alloy Chemical Composttion (%)
Kanthu	AWS		Cu	Si	Fe	Mn	Mg	Cr	Zn	Ti	AL
Aluminium Yoyera	Mtengo wa ER1100		0.05-0.20	1.00		0.05			0.10		99.5
	Mtengo wa ER1100		0.05-0.20	1.00		0.05			0.10		99.5	Pulasitiki wabwino, kuwotcherera gasi zoteteza kapena argon arc kuwotcherera kwa dzimbiri zosagwira aluminiyamu koyera.
	Aluminiyamu Aloyi	Mtengo wa ER5183		0.10	0.40	0.40	0.50-1.0	4.30-5.20	0.05-0.25	0.25	0.15	Rem
Kulimba kwakukulu, kukana kwa dzimbiri, kwa kuwotcherera kwa argon arc.
Mtengo wa ER5356			0.10	0.25	0.40	0.05-0.20	4.50-5.50	0.05-0.20	0.10	0.06-0.20	Rem
Kulimba kwakukulu, kukana kwa dzimbiri, kwa kuwotcherera kwa argon arc.
Mtengo wa ER5087			0.05	0.25	0.40	0.70-1.10	4.50-5.20	0.05-0.25	0.25	0.15	Rem
Kukana bwino kwa dzimbiri, weldability ndi pulasitiki, kuwotcherera gasi zoteteza kapena kuwotcherera argon arc.
Mtengo wa ER4047			0.30	11.0-13.0	0.80	0.15	0.10		0.20		Rem
Makamaka kwa brazing ndi soldering.
Mtengo wa ER4043			0.30	4.50-6.00	0.80	0.05	0.05		0.10	0.20	Rem
Kukana bwino kwa dzimbiri, kugwiritsa ntchito kwakukulu, chitetezo cha gasi kapena kuwotcherera kwa argon acr.