Nichrome / Kutentha ElementResistance Waya/ Flat Waya
Ni80Cr20ndi nickel-chromium alloy (NiCr alloy) yodziwika ndi kukana kwambiri, kukana kwa okosijeni wabwino komanso kukhazikika kwa mawonekedwe abwino kwambiri.Ndi yoyenera kugwiritsidwa ntchito pa kutentha mpaka 1200 ° C, ndipo imakhala ndi moyo wapamwamba wa utumiki poyerekeza ndi ma aloyi a Iron chromium aluminium.
Ntchito zofananira zaNi80Cr20ndi zinthu zotenthetsera zamagetsi pazida zam'nyumba, ng'anjo zam'mafakitale ndi zopinga (zopinga mawaya, zotchingira mafilimu azitsulo), zitsulo zosalala, makina akusita, zotenthetsera madzi, kuumba pulasitiki kumafa, zitsulo zomangira, zitsulo zomata ndi zinthu za cartridge.
Zomwe zili bwino%
C | P | S | Mn | Si | Cr | Ni | Al | Fe | Zina |
Max | |||||||||
0.03 | 0.02 | 0.015 | 0.60 | 0.75-1.60 | 20.0-23.0 | Bali. | Kuchuluka kwa 0.50 | Kuchuluka kwa 1.0 | - |
Makina Okhazikika (1.0mm)
Zokolola mphamvu | Kulimba kwamakokedwe | Elongation |
Mpa | Mpa | % |
420 | 810 | 30 |
Zodziwika bwino zakuthupi
Kuchulukana (g/cm3) | 8.4 |
Kulimbana ndi magetsi pa 20ºC(mm2/m) | 1.09 |
Coefficient ya conductivity pa 20ºC (WmK) | 15 |
Coefficient ya kukula kwa kutentha | |
Kutentha | Coefficient of Thermal Expansion x10-6/ºC |
20 ºC-1000ºC | 18 |
Kuchuluka kwa kutentha kwapadera | |
Kutentha | 20ºC |
J/gK | 0.46 |
Malo osungunuka (ºC) | 1400 |
Kutentha kosalekeza kosalekeza mumlengalenga (ºC) | 1200 |
Maginito katundu | wopanda maginito |
Kutentha Zinthu Za Magetsi Resistivity | |||||
20ºC | 100ºC | 200ºC | 300ºC | 400ºC | 600ºC |
1 | 1.006 | 1.012 | 1.018 | 1.025 | 1.018 |
700ºC | 800ºC | 900ºC | 1000ºC | 1100ºC | 1300ºC |
1.01 | 1.008 | 1.01 | 1.014 | 1.021 | - |
Mtundu wa kaperekedwe
Dzina la Alloys | Mtundu | Dimension | ||
Ni80Cr20W | Waya | D = 0.03mm ~ 8mm | ||
Mtengo wa Ni80Cr20R | Riboni | W=0.4~40 | T=0.03~2.9mm | |
Ni80Cr20S | Kuvula | W = 8 ~ 250mm | T=0.1~3.0 | |
Ni80Cr20F | Chojambula | W = 6 ~ 120mm | T=0.003~0.1 | |
Ni80Cr20B | Malo | Dia = 8 ~ 100mm | L=50~1000 |